Multihydroxyl End Functional Polyethylenes: Synthesis, Bulk and Interfacial Properties of Polymer Surfactants
Kimani, S.M.; Thompson, R.L.; Hutchings, L.R.; Clarke, N.; Billah, S.M.R.; Sakai, V.G.; Rogers, S.E.
Dr Richard Thompson firstname.lastname@example.org
Lian Hutchings email@example.com
Multihydroxyl end functional polyethylenes have been prepared with controlled molecular weight, microstructure, and functionalization. These materials, designed as interfacially active blend additives for polar interfaces, are thermally stable up to 250 °C and to have similar crystallinity and dynamics to their unfunctionalized homopolymer analogues. The polymers segregated strongly to silicon oxide interfaces, with adsorbed layers forming spontaneously at annealed polymer interfaces, having surface excess concentrations approaching 2Rg and a maximum areal density of approximately 0.6 adsorbed chains per nm2. This interfacial activity is achieved almost without detriment to the bulk physical properties of the polymer as evidenced by thermal analysis, quasi-elastic neutron scattering, and small-angle neutron scattering (SANS). SANS experiments show little evidence for aggregation of the dihydroxyl functionalized polymers in blends with PE homopolymers, which is thought to explain why these additives have particularly strong interfacial adsorption, even at relatively high concentrations. A modest level of segregation of the additives to exposed blend surfaces was also seen, particularly when the additive molecular weight was significantly lower than that of the matrix. We attribute this to a combination of the relatively low molecular weight of the additives and the marginally lower surface energy associated with deuterated polymers.
Kimani, S., Thompson, R., Hutchings, L., Clarke, N., Billah, S., Sakai, V., & Rogers, S. (2014). Multihydroxyl End Functional Polyethylenes: Synthesis, Bulk and Interfacial Properties of Polymer Surfactants. Macromolecules, 47(6), 2062-2071. https://doi.org/10.1021/ma402158b
|Journal Article Type||Article|
|Publication Date||Mar 1, 2014|
|Deposit Date||Mar 20, 2014|
|Publicly Available Date||Mar 27, 2014|
|Publisher||American Chemical Society|
|Peer Reviewed||Peer Reviewed|
Accepted Journal Article
This document is the Accepted Manuscript version of a Published Work that appeared in final form in Macromolecules, copyright © American Chemical Society after peer review and technical editing by the publisher. To access the final edited and published work see http://dx.doi.org/10.1021/ma402158b
You might also like
The influence of ambient cure chemistry and stoichiometry on epoxy coating surfaces
Modulated Fluorescence in LB Films Based on DADQs—A Potential Sensing Surface?
Synthesis and characterisation of a mussel-inspired hydrogel film coating for biosensors