Biotribological and Structural Analyses of Large Diameter Ceramic on Carbon Fibre Reinforced PEEK Hip Joints with Different Inclination
(2011)
Presentation / Conference Contribution
Outputs (7)
Prosim Simulator Wear Study of 60mm Diameter Zirconia Toughened Alumina Composite Hip Bearings: The Effect of High Cup Inclination Angle and Microseparation (2011)
Presentation / Conference Contribution
Excellent Performance of Novel Hip Bearings with Third Generation Superlattice Coating (2011)
Presentation / Conference Contribution
Biotribology of 40mm Diameter MOTIS PEEK on Ceramic Hip Joints: A Detailed Simulator Study with Different Inclination Angles (2011)
Presentation / Conference Contribution
Modelling of permeability loss in membrane filtration: Re-examination of fundamental fouling equations and their link to critical flux (2011)
Journal Article
A re-evaluation of the flux decline relationships in the appendix of the 1995 critical flux paper has failed to establish that one may have a critical flux in the presence of fouling that is represented by the “complete” pore blocking (n = 2) mode. I... Read More about Modelling of permeability loss in membrane filtration: Re-examination of fundamental fouling equations and their link to critical flux.
Wear and surface analysis of 38 mm ceramic-on-metal total hip replacements under standard and severe wear testing conditions (2011)
Journal Article
The purpose of this study was to compare the wear of zirconia-toughened alumina (ZTA) and alumina femoral heads tested against as-cast CoCrMo alloy acetabular cups under both standard and severe wear conditions. A new severe test, which included medi... Read More about Wear and surface analysis of 38 mm ceramic-on-metal total hip replacements under standard and severe wear testing conditions.
Oxidation and fusion defects synergistically accelerate polyethylene failure in knee replacement (2011)
Journal Article
We have previously reported upon a cohort of patients with premature failure of such material and postulated upon the impact of abnormally high concentrations of type 2 fusion defects whereby there is a lack of particle cohesion due to incomplete dif... Read More about Oxidation and fusion defects synergistically accelerate polyethylene failure in knee replacement.